Titanium oxide Nanopowder, anatase phase
Along with the listed NanoCeramics many other ceramics were produced as trial batches, e.g. NanoCeramics from Rare Earth Oxides, HfO2, MgO+C, TiO2, TiC, TiN, BN, Y2O3 Basic technology permits to produce nearly any ceramic in nanosized form, thus we are expecting here the concrete wishes from our customers.
Description
| Produced by chemical synthesis; Dry nanopowder, free of organic stabilizers. |
| Average particle size: 4-8 nm. |
| Easily forms collidal solutions in water; Can be used to produce coatings. |
Pack Sizes
| Catalogue No. | Quantity |
| RN - PL - TiO-NO-10g | 10g |
| RN - PL - TiO-NO-50g | 50g |
TiO2 - Nanoparticles aqueous suspension, anatase phase
Properties
| Produced by chemical synthesis |
| Average particle size: 4-8 nm. |
| Aqueous colloidal solutions: 5, 10 or 20 wt.% |
Aqueous colloidal solution, 5 wt.%22
Pack Sizes
| Catalogue No. | Quantity |
| RN - PL - TiO-5p-10g | 200mL |
| RN - PL - TiO-5p-50g | 1000mL |
Aqueous colloidal solution, 10 wt.%
Pack Sizes
| Catalogue No. | Quantity |
| RN - PL - TiO-10p-10g | 100mL |
| RN - PL - TiO-10p-50g | 500mL |
Aqueous colloidal solution, 20 wt.%
Pack Sizes
| Catalogue No. | Quantity |
| RN - PL - TiO-20p-10g | 50mL |
| RN - PL - TiO-20p-50g | 250mL |
TiO2 - Nanoparticles, type P25
Properties
| Photocatalytic standard P25; Dry Nanopowder. Mixed rutile / anatase phase |
| Average primary particle size: 21±5 nm; Tapped density: ca. 130 g/L |
| Specific surface: 50±10 m2/g Purity after ignition: >99,5% |
| Ignition loss: < 2%; Moisture: < 1,5% Al2O3 < 0,3 wt.%; SiO2 < 0,2 wt.% ; |
Pack Sizes
| Catalogue No. | Quantity |
| RN - PL - TiO-P25-10g | 10g |
| RN - PL - TiO-P25-50g | 50g |
TiO2 - Nanoparticles, type P25, hydrophobized
Description
| Photocatalytic standard P25; Dry Nanopowder. Mixed rutile / anatase phase |
| Average primary particle size: 21±5 nm; Tapped density: ca. 130 g/L |
| Specific surface: 50±10 m2/g Purity after ignition: >99,5% |
| Ignition loss: < 2%; Moisture: < 1,5% Al2O3 < 0,3 wt.%; SiO2 < 0,2 wt.% |
Pack Sizes
| Catalogue No. | Quantity |
| RN-PL-TiO-N-20p-15g | 75ml |
| RN-PL-TiO-N-20p-50g | 250ml |
TiO2 - Nanoparticles, rutile
Description
| Average particle size: 2±1 nm. Dry nanopowder. |
| Readily forms aqueous colloidal solutions in water(up to 900g/L) and methanol |
Pack Sizes
| Catalogue No. | Quantity |
| RN - PL - TiO-R-1g | 1g |
| RN - PL - TiO-R-5g | 5g |
| RN - PL - TiO-R-25g | 25g |
TiO2 - Nanoparticles aqueous suspension, brookite/anatase
Description
| Average particle size: 2-5 nm. Mixed brookite / anatase phase. |
| Stabilized by tetramethylammoniumhydroxide; Aqueous colloidal solution 20 wt.% |
Pack Sizes
| Catalogue No. | Quantity |
| RN - PL - TiO-N-20p-15g | 75ml |
| RN - PL - TiO-N-20p-50g | 250ml |
TiO2 - Nanopowder, anatase, hydrophobic
Description
| Average particle size: 4-8 nm. Anatase phase; Supplied as a powder |
| Stabilized by dodecylphosphonic acid and hexylamine. |
| Forms transparent colloidal solutions in chloroform. |
Pack Sizes
| Catalogue No. | Quantity |
| RN - PL - TiO-HPBC-1g | 1g |
| RN - PL - TiO-HPBC-10g | 10g |
TiO2 - Nanoparticles, anatase, hydrophobic Solution
Description
| Average particle size: 4-8 nm. Anatase phase; Supplied as a 100 g/L solution in MEK. |
| Stabilized by benzoic acid |
| Forms transparent colloidal solutions in MEK (methylethylketone) and epoxides. |
Pack Sizes
| Catalogue No. | Quantity |
| RN - PL - TiO-HPBM-10p-1g | 10ml |
| RN - PL - TiO-HPBM-10p-10g | 100ml |